Waxes currently used as a coating material to preserve surfaces of outdoor iron sculptures tend to face lower coating strength and efflorescence due to the aging from air pollution and acid rains. Consequently, they are subjected to repeated corrosions shortly after the treatment. And the sculptures face the problem losing their original nature because of the changes of colors and lusters, so this convergence study aims at developing wax with better performance than the existing materials. For this reason, the study identified the effects of physical property using the environmental experiments such as the tests of salt spray and gas corrosion as well as the analysis of luster level and thermo-gravimetry. As this study result, the developed ISC wax showed the excellent blocking effect from salt water and coating durability more than five times compared with the existing waxes, better acid resistance by two-four times, sun block effect by 2-10 times, improved luster variance by 3-16 times, improved thermo-stability and durability by 0.5-5 times, and therefore demonstrating far better coating effect than the existing waxes. In the light of these findings, this study contributes for this new development which can replace the existing waxes used so far in order to preserve the outdoor iron sculptures.

한국어

야외 철제 조각 작품 표면 보존용 코팅제로 사용되고 있는 왁스는 대기의 오염과 산성비 등에 의해 노화되어 코팅력 이 저하되고 백화현상이 발생하며, 이로 인해 보존처리 후 짧은 시간 내에 재 부식이 발생한다. 또한 색상 및 광택 변화가 일어나 작품 본래의 특성을 잃어버리는 등의 문제점이 나타나고 있어 융합 연구를 통해 기존 재료보다 성능이 개선된 왁스 를 개발하고자 하였으며, 염수 분무, 가스 부식 실험 등의 환경실험과 광택도, 열 중량 분석을 통해 물성 효과를 확인하였다. 실험 결과 개발된 ISC왁스는 기존 왁스에 비해 염수로부터 5배 이상의 우수한 차단성과 코팅 지속력을 보여주었으며, 2～4 배 이상의 내산성, 2～10배 이상의 자외선 차단성, 3～16배 이상의 증진된 광택 변화량, 0.5～5배 이상의 내열성과 내구성 등을 나타내 기존 왁스 보다 우수한 코팅 효과를 나타내었다. 이러한 결과로 보아 야외 철제 조각 작품 보존처리에 사용되어 온 기존의 왁스를 대체할 수 있는 재료로 판단된다.