earticle

영어

In this study, to verify the environmental property of eco-friendly solidification material using porous silica in forest road, a pH property test, solubility test, and fish toxicity test have been performed. As a result of pH property test, mixed soil of eco-friendly solidification material showed pH of 7.09 from clay, pH of 6.67 from organic soil, and pH of 7.15 from weathered soil, and in case of cement mixed soil, clay showed pH of 9.82, organic soil showed pH of 9.15, and weathered soil showed pH of 9.35, showing mixed soil of solidification material to have lower pH value than cement mixed soil. In the solubility test, 0.04mg/ℓ of lead and 0.004mg/ℓ of CN were found, but Cd, Cu, Fg, Cr6+, As, and org.P were not found to show that all of them do not exceed the standards of hazardous waste. In the fish toxicity test, within the initial 24 hours, all fish died from cement, while no fish died from eco-friendly solidification material. Likewise, in all hazardousness tests, eco-friendly solidification material showed lower hazardousness than cement.

한국어

본 연구는 임도의 포장재로 사용할 수 있는 다공성 실리카를 이용한 친환경 고화재 의 환경성을 검증하기 위해 pH특성 시험과 용출 시험, 어독성 시험을 수행하였다. pH 특성 시험결과, 친환경 고화재 혼합토의 경우 점토는 pH 7.09, 유기질토는 pH 6.67, 그 리고 풍화토는 pH 7.15로 나타났으며, 시멘트 혼합토의 경우 점토는 pH 9.82, 유기질토 는 pH 9.15, 그리고 풍화토는 pH 9.35로 나타나 고화재 혼합토가 시멘트 혼합토 보다 pH값이 다소 낮게 나타났으며, 또한 용출 시험에서는 Pb이 0.04mg/ℓ, CN이 0.004mg/ ℓ로 소량이 검출되었으나 Cd, Cu, Fg, Cr6+, As, org.P의 기타 항목에서는 검출되지 않 아 모든 항목이 유해폐기물 기준치를 초과하지 않는 것으로 나타났다. 어독성 시험결과 는 초기 24시간 내 시멘트의 경우 공시어가 모두 치사한 반면 친환경 고화재의 경우는 치사율이 0%로 나타났다. 이와 같이 모든 유해성 시험에서 친환경 고화재가 시멘트보 다 유해성이 적은 것으로 나타났다.