원문정보
피인용수 : 0건 (자료제공 : 네이버학술정보)
초록
영어
Nickel oxide nanofibers were synthesized by electrospinning with nickel(II) acetate tetrahydrate and polyvinylpyrrolidone and calcination process. The nanofiber shape was easily detected from the nanofibers with high Ni contents after calcined at 600oC and the crystal structure of layer-by-layer growth was observed from SEM images at 900oC. XRD and TEM results showed metallic Ni and NiO structure were formed at nanofibers obtained at 600 and 900oC and the crystallite size was calculated from 25 to 55 nm. The surface of nanofibers was fully oxidized from the deconvoluted Cu 2p and O 1s XPS spectra.