Fire-Protection Method to Improve the Fire-Resistance Capacity of Near-Surface-Mounted Fiber Reinforced Polymer
초록
영어
Recently, retrofit by using fiber reinforced polymer (FRP) has been widely applied to building structure. However, the retrofit contribution of FRP may be disappeared under high temperature such as fire loading because of the low glass transition temperature of FRP and epoxy. In this manner, this paper presents a research for improving fire resistant capacity of FRP retrofit system. Heat transitions of two types of fire proofing materials (board type and spray type) were verified by performing high temperature loading test and heat transfer analysis. As a result, it was found that the board made of calcium silicate and alumino silicate had higher resistance on the heat transition than the sprayed finish. By using the analytical approach, it is possible to properly estimate the heat transfer of fire-proofing with board under high temperature environment for fir-resistance design of reinforced FRP.
한국어
최근 섬유보강 폴리머 (FRP)를 이용한 건물의 보강이 널리 적용되고 있다. 그러나, 화재 등에 의해서 높은 온도에 노출될 경우, FRP와 에폭시의 낮은 유리전이온도특성 때문에 이 보강방법은 보강효과를 상실하게 된다. 이와 같은 측면에서, 본 논문에서는 FRP 보강시스템의 화재저항 성능을 향상시키기 위한 연구를 진행하였다. 특히 이들 재료들의 내화특성을 파악하기 위하여 실험과 열전도 해석을 실시하여 온도전달특성을 밝혔다. 연구를 통하여, 칼슘실리케이트와 알루미노 실리케이트는 열 저항성능이 높다는 것이 확인되었고 유한요소해석을 통하여 내화재의 두께를 설계하기 위한 열전도 특성의 예측이 가능한 것으로 나타났다.
목차
1. 서론
2. 기존연구 분석
3. 내화단열 성능 실험
3.1 실험계획
3.2 실험방법
3.3 실험결과
3.4 내부온도의 변화 비교
4. 열전도 해석
4.1 해석 개요
4.2 해석결과 및 분석
5. 결론
REFERENCES