양생온도가 전기로 산화슬래그를 사용한 고강도 모르타르의 자기수축에 미치는 영향

원문정보

Effect of Curing Temperature on the Autogenous Shrinkage of High Strength Mortar Using Electric Oxidizing Arc Slag

한민철

피인용수 : 0(자료제공 : 네이버학술정보)

초록

영어

The objective of this study is to investigate the effect of the replacement of electric oxidizing arc slag fine aggregates(EFA) on the autogenous shrinkage of high strength mortar with 80 MPa subjected to various curing temperatures and to estimate the autogenous shrinkage development by applying maturity method. EFA is replaced by limestone fine aggregates from 25%, 50% and 100%. Curing temperatures are fixed at 5℃, 20℃ and 35℃, respectively. Equivalent age is calculated based on ASTM C 1074 to estimate autogenous shrinkage development. Test results indicate that replacement of EFA resulted in an increase of compressive strength at 35 ℃, while it decreased compressive strength at 5℃. Autogenous shrinkage was reduced with increase of EFA replacement and this tendency is more clear when the specimens were cured at 35℃. This may be due to the presence of free-CaO in EFA. Non linear regression model based on Exponential growth curve was applied to estimate autogenous shrinkage with equivalent age. Predicted values had relatively good agreement with measured ones.

목차

Abstract
 1. 서론
 2. 실험계획 및 방법
  2.1 실험계획
  2.2 사용재료
  2.3 실험방법
 3. 실험결과 및 분석
  3.1 양생온도별 응결시간
  3.2 양생온도별 압축강도 증진
  3.3 양생온도별 자기수축 특성 및 해석
 4. 결론
 REFERENCES

저자정보

  • 한민철 Han, Min-Cheol. 청주대학교 건축공학과 부교수, 공학박사

참고문헌

자료제공 : 네이버학술정보

    함께 이용한 논문

      ※ 기관로그인 시 무료 이용이 가능합니다.

      • 4,000원

      0개의 논문이 장바구니에 담겼습니다.