Preliminary evaluation of concrete basic properties of porous structure with repair performance for application to conservative pavement method to control urban heat island phenomenon is very important. Particularly, various factors such as cement strength, aggregate strength, major porosity, and curing are important factors related to the strength of porous concrete. As a result of measuring the surface temperature change of the water-retaining block, the composition satisfying the above property values was compared with the general packing block. The surface temperature increased from 5.1 ℃ to 10.1 ℃ for about 15 min to 120 min due to the increase of water retention and absorbability due to the large amount of pores existing in the inside when exposed to electric heat. The mixing condition to satisfy the bending strength of 3.0 MPa or more, the water content of 0.15 g/cm3 or more, and the absorption height of 70% or more together with a large amount of pores in the water-retaining concrete block is an aggregate size of 1.0mm to 2.5mm, an eco-binder. It was confirmed that the total porosity in the block was satisfactory at 18% ~ 20%, and that the optimal polymer blend composition was about 5.0 wt% to simultaneously improve the bending strength, water retention and water absorbing properties.

한국어

도시 열섬 현상을 제어하기위한 보수 포장 방법에 대한 수리 성능을 갖는 다공성 구조물의 콘크리트 기본 특성에 대한 예비 평가는 매우 중요하다. 특히, 시멘트 강도, 골재 강도, 주요 다공성 및 경화와 같은 다양한 요소가 다공성 콘크리트의 강도와 관련된 중요한 요소이다. 본 연구에서는 굴곡 강도 3.0MPa 이상, 함수율 0.15g / ㎤ 이상의 기본 물성치를 만족하는 최적의 기공율 및 품질 규격치 향상을위한 고분자 혼련 물의 양 및 70 % 이상의 흡수가 유도되었다. 실험에 의해 적용된 최적의 조성을 위해, 기본 콘크리트 포장 블록과 비교하여 표면 온도 변화가 측정되었다. 이 때 10 분 동안 5.1 ℃ 이상으로 열을 감소시키는 효과가 있었다.