초록

영어

We have fabricated and characterized 32 × 32 photonic quantum ring (PQR) laser arrays uniformly operable with 0.98 ㎂ per ring at room temperature. The typical threshold current, threshold current density, and threshold voltage are 20 mA, 0.068 A/cm2, and 1.38 V. The top surface emitting PQR array contains GaAs multiquantum well active regions and exhibits uniform characteristics for a chip of 1.65 × 1.65 mm2. The peak power wavelength is 858.8 ± 0.35 nm, the relative intensity is 0.3 ± 0.2, and the linewidth is 0.2 ± 0.07 nm. We also report the wavelength division multiplexing system experiment using angle-dependent blue shift characteristics of this laser array. This photonic quantum ring laser has angle-dependent multiple-wavelength radial emission characteristics over about 10 nm tuning range generated from array devices. The array exhibits a free space detection as far as 6 m with a function of the distance.

한국어

상온에서 단일소자의 경우 0.98 ㎂ 문턱전류를 나타내는 32 × 32 광양자테 레이저 어레이를 제작하였다. 제작된 어레이의 전체 소자들의 문턱전류 및 밀도, 전압은 20 mA, 0.068 A/cm2, 1.38 V의 값을 나타내었다. 발광 광양자테 어레이는 GaAs 물질이 다중-양자 우물 활성 영역을 구성하고, 칩이 차지하는 면적은 1.65 × 1.65 mm2였 으며, 소자들의 피크파워 파장은 858.8 ± 0.35 nm, 상대적인 레이저 세기는 0.3 ± 0.2, 선폭은 0.2 ± 0.07 nm로 비교적 균일한 특성을 보였다. 또한, 레이저 어레이의 각도 의존적 청색 이동 특성을 이용한 파장 분할 멀티플렉싱 시스템 실험을 진행하였고, 각도에 따라 10 nm 정도 파장이 변하는 현상을 발견하였으며, 거리에 따른 레이저 세기 를 측정한 결과 6 m에서도 감지할 수 있음을 확인하였다.

목차

Abstract
 요약
 1. INTRODUCTION
 2. Experimental Details
 3. Results and Discussions
 4. Summary
 ACKNOWLEDGMENTS
 REFERENCES

저자정보

  • Jongpil Lee 이종필. Department of Renewable Energy, Jungwon University
  • Moojin Kim 김무진. Department of Renewable Energy, Jungwon University

참고문헌

자료제공 : 네이버학술정보

    함께 이용한 논문

      ※ 기관로그인 시 무료 이용이 가능합니다.

      • 4,000원

      0개의 논문이 장바구니에 담겼습니다.