The bonding interface microstructure and mechanical property of clad plate with different hot rolling schedules were researched. The results show that the carbide layer thickness of bonding interface increases firstly and then decreases with increasing reduction ratio. The carbide layer of bonding interface is the major factor relating to tensile strength, so the experimental values of clad plate are slightly higher than the calculated ones. Moreover, the bending strength of clad plate is mainly influenced by the thickness ratio and the carbide quantity of SS, while the carbide layer thickness of bonding interface is an important factor affects the bending strength.