지르코니아의 소결 후 특성

원문정보

Surface Characteristics of Ground and Post-Sintered Zirconia

김민정, 김임선, 최병환, 김원기

피인용수 : 0(자료제공 : 네이버학술정보)

초록

영어

Purpose: It is to compare and evaluate the change of the wear rate and phase variation of the Zirconia before and after the sintering after the grinding by a high speed equipment manufactured for the Zirconia. Methods: The specimen of the sintered Zirconia was manufactured as size of 15㎜×15㎜×2㎜. The grinding has been applied to each of all pieces of each test groups for a minute fit for each condition at same speed of 50,000 rpm by a diamond bur at high speed handpiece with injection of the air and water. For the observation of the surface before and after the sintering of the each test piece, the cross section of it was observed as 100 magnification by a scanning electron microscope after it was coated by PT, and the diffraction analysis was performed by XDR to compare the crystal phase of the Zirconia. The average surface roughness value of all specimens were evaluated. The wear test was performed at room temperature by applying a load of 1kg for 120,000 cycles for the chewing period 6 months. Wear was analyzed for the enamel cusps by measurement of the vertical substance loss with a laser scanner. Conclusion: The phase variation from the tetragonal phase to the monoclinic phase was confirmed in the test group of the pre-sintered Zirconia after the grinding, and the value of the surface roughness and the wear rate was increased in experimental group.

목차

Abstract
 Ⅰ. 서론
 Ⅱ. 연구 방법
  1. 시편 제작
  2. 실험 방법 및 분석
  3. 통계 분석
 Ⅲ. 결과
 Ⅳ. 고찰
 Ⅴ. 결론
 REFERENCES

저자정보

  • 김민정 Min-Jeong Kim. 경북대학교 의용생체공학과
  • 김임선 Im-Sun Kim. 대구보건대학교 치기공과
  • 최병환 Byung-Hwan Choi. 대구보건대학교 치기공과
  • 김원기 Won-Gi Kim. 대구보건대학교 치기공과

참고문헌

자료제공 : 네이버학술정보

    함께 이용한 논문

      ※ 기관로그인 시 무료 이용이 가능합니다.

      • 4,000원

      0개의 논문이 장바구니에 담겼습니다.