This study is to be suggest the optimal mat foundation mixing design of high strength concrete by using fly ash and retarding admixture. This study applied retarding admixture to high strength concrete over 40MPa, and tested the mechanical properties of concrete according to binder content(385∼415kg/㎥), fly ash substitution rate(0~25%), and adding rate of retarding admixture(0~1.2%) As a results, For the concrete to be applied to lower part of mat foundation, it is suitable to substitute FA 25% with binder contents 385kg/㎥ and to apply the mixing with adding retarding admixture 1% in order to repress hydration heat and to cast concrete at once through congelation delay. As a result of experiments of adiabatic temperature rising, coefficients of adiabatic temperature rising K and α were 40.68 and 1.08 for retarding-type concrete and 42.8 and 1.13 for standard concrete, respectively, under the condition of initial concrete temperature about 19℃. In the identical temperature condition, differences of adiabatic temperature rising speed according to use of retarding admixture were not different, and maximum value of adiabatic temperature rising of retarding-type concrete was lower than standard concrete.

한국어

본 연구에서는 플라이애쉬와 지연제를 사용한 고강도 콘크리트의 매트기초 최적 배합설계를 제시하고자 하는 연구이다. 본 연구는 40MPa이상의 고강도 콘크리트에서 결합재량(385∼415kg/㎥), 플라이애시 치환율(0∼25%), 지연제 첨가율(0∼1.2%)에 따른 콘크리트의 역학적 특성을 평가하였다. 그리고 결과는 다음과 같다. 매트기초 하부에 적용할 콘크리트는 수화열 발생을 억제하고 응결지연을 통한 일체 타설을 위해 결합재량 385kg/㎥에 FA를 25% 치환하고 지연제를 1% 사용한 배합을 적용적용하는 것이 바람직한 것으로 판단된다. 단열온도상승 실험 결과, 단열온도상승 계수 K값과 α값은 콘크리트 초기온도 약 19℃ 조건에서 지연형 콘크리트는 40.68과 1.08, 표준형 콘크리트는 42.8과 1.13로 나타났다. 동일 온도조건에서 지연제 사용에 따른 단열온도 상승속도 차이는 크지 않으며, 지연형 콘크리트의 최대 단열온도상승값이 표준형 콘크리트 대비 낮게 나타났다.