This paper is a tentative first study on preventive methods of air and oil leakage problems of the composite rubberized polymer gels. During stirring phase, the physical property changes are examined as well as the degree of physical recovery of the material was taken as a base data and set as reference. The leakage of gel is mostly influenced by properties changes caused by too much stress of materials themselves occurring when the physical rotational force is applied through the agitator to secure the construct ability of gel that has the strong rubber characteristic due to material features for construction. Based on this data, attempts were made to reduce the deterioration of physical properties during stirring and a standardized stirring method that allows recovery of the material after application was determined. The evaluation criteria was centered on the properties changes that follow during the total time for stirring, and the appropriate stirring time in regards to preventing air and oil leakage during application in construction sites was determined to be approximately 15 minutes.

한국어

본 연구는 최근 지속적으로 발생하고 있는 합성고무계 폴리머 겔의 누출 및 누유 현상을 방지하기 위한 첫 번째 연구로써 교반시간에 따른 물성변화 특성을 파악하고, 교반 후 시간 경과에 따른 물성 회복 정도에 대한 기초적 데이터 구축을 기본으로 하여, 이를 기반으로 교반에 의한 물성 저하를 최소화하고 시공 후 물성회복이 가능한 적정 교반 기준 마련하는데 그 목적을 두었다. 겔재의 누유현상은 시공 시 재료 특성 상 고무적인 성질이 강한 겔재의 시공성을 확보할 목적으로 교반장비를 통해 물리적인 회전력을 가함으로써 발생하는 재료자체의 과도한 스트레스로 인한 물성변화가 가장 큰 원인으로 작용한다. 평가는 교반시간에 따른 점도 특성 및 물성 변화 특성을 중심으로 진행하였으며, 본 연구결과를 종합하였을 때, 교반에 의한 물성 저하를 최소화하고 시공 후 물성회복이 가능한 범위로써, 현장에서 겔재의 교반 시 시공 후 저점도 현상에 따른 누유현상 및 누출현상을 방지하기 위한 적정 교반 시간은 약 10분 내외가 될 것으로 사료된다.