We stuidied liauid crystal alignment treatment using solution process for making thin oxide layer in liquid crystal display. It is the one of very effient and popular process in making thin oxide layer in electronical industrial fields. Particularly, this process has highly potential value in liquid crystal display industrial fields because it cause automatically induced alignment process without tranditional alignment process in liquid crystal alignment process. We made several different kinds of mol density solutions using strontium oxide solution. And those solutions were treated for solidification layers using annealing process for 2 hours. And we stuided pretilt angle properties of these alignment layers of strontium oxide for clarifying the relationship of liquid crystal molecules and thin strontium oxide layer. And we also tested the existence of strontium oxide thin layer on substrate using XPS measurement. We expected the hig gain of electro-optical properties in liquid crystal display using strontium oxide thin layer because it has high K property material than the other metal-based oxide layers. In this results, we measured 1.447 to 1.613 thresholds volts as 0.1 mol to 0.4 mol density in 0.1 mol density steps. This is significant better characteristics than conventional liquid crystal display as higher than 1.85 thresholds volts. And it make possible to making next-generation liquid crystal display which present low-power consumption and wide gray scale in liquid crystal display.

한국어

본 연구에서는 Solution Process를 적용한 Strontium Oxide를 배향막으로 사용한 경우의 액정배향 특성에 대해서 연구하였다. Stronium Oxide 는 High K 물질로 배향막으로 사용할 경우 임계치 전압을 효율적으로 조절할 수 있는 장점이 있으나, 액정분자와의 배향에 관한 상호관계에 대해서는 많은 연구가 진행되지 않았었다. 0.1～0.4 Mol 롤 농도를 조절한 Strontium Oxide를 Solution Process 로 배향막으로서 제조함으로써, 보다 생산성이 좋은 방법을 제시할 수 있었으며, 재료가 갖는 우수한 특성을 반영한 액정디 스플레이의 제조가 가능하였다. 샘플 측정결과 1.447～1.613V 의 임계치 전압특성을 보여주어 기존의 방법으로 제조된 액정디스플레 이와 동등 혹은 우월한 특성을 갖고 있음을 알 수 있었다.