In this study, a scintillation detector was fabricated using a silicon photomultiplier (SiPM) and a Ce:GAGG scintillator single crystal, and its spectroscopic properties were compared with those of commercially available LYSO and CsI:Tl scintillators using γ-ray spectroscopy. The energy resolutions of the self-produced scintillation detector composed of the scintillator single crystal (volume: 3 × 3 × 20 mm3) and SiPM (Photosensitive area: 3 × 3 mm2) for standard γ-ray sources, such as 133Ba, 22Na, 137Cs and 60Co were measured and compared. As a result, the energy resolutions of the proposed Ce:GAGG scintillation detector for g-rays, as measured using its spectroscopic properties, were found to be 13.5% for 133Ba 0.356 MeV, 6.9% for 22Na 0.511 MeV, 5.8% for 137Cs 0.662 MeV and 2.3% for 60Co 1.33 MeV.

한국어

본 연구에서는 실리콘 광 증배소자(Silicon photomultiplier)와 Ce:GAGG 섬광체 단결정을 이용한 섬광검출기를 제작 하고, 감마선 분광특성 분석을 통해 기존에 상용화된 LYSO, CsI:Tl 섬광체와의 분광특성을 비교하였다. 섬광체 단결 정의 크기는 3 × 3 × 20 mm3 이며 3 × 3 mm2 실리콘 광 증배소자를 이용하여 섬광검출기를 제작한 후, 표준 감마 선원인 133Ba, 22Na, 137Cs, 60Co에 대한 에너지 분해능을 각각 측정하고 비교하였다. 그 결과 Ce:GAGG 섬광검출기의 감마선에 대한 에너지 분해능은 133Ba 0.356 MeV에서 13.5%, 22Na 0.511 MeV에서 6.9%, 137Cs 0.662 MeV에서 5.8% 그리고 60Co 1.33 MeV에서 2.3%의 분광 특성을 확인 할 수 있었다.