The purpose of this study is to investigate mechanical properties of bonding technique using nano-slag and alkaline activator. As a results is following. The compressive strength of horizontality placing jointed 3day after placement of concrete containing nano-slag and potassium hydroxide had more effective than other specimens at 3 days. And flexural strength containing calcium hydroxide had more effective than other specimens. The compressive strength of horizontality placing jointed 7day after placement of concrete containing nano-slag and alkaline activators(Na, Ca, Na) had more effective than O.P.C at 7 days. The flexural strength containing nano-slag and calcium hydroxide had more effective than other specimens at 3 and 7 curing days and they showed a similar strength of plain at 28 curing day. Therefore, it showed that the strength and flexural of horizontality placing jointed concrete by dissolving alkaline activators and nano-slag had more effective than non-agent horizontality placing jointed concrete.

한국어

나노슬래그와 알칼리자극제를 활용하여 레이턴스 면의 접합기술에 관한 역학적 특성 고찰결과 다음과 같은 결론을 얻었다. 3일후 이어치기 압축강도 측정결과 재령 3일에서는 나노슬래그에 수산화칼륨(Ka)을 혼입한 조건에서 강도 증진이 가장 우수 하였으나, 복합조건에서는 수산화칼륨 및 3종 모두를 사용한 조건에서 최대강도가 확인되었다. 3일후 이어치기 휨강도 측정결과 나노슬래그(N.S)에 알칼리자극제(Na, Ca, Ka)를 각각 단독 사용한 조건에서는 압 축강도 결과와 달리 재령 3일에서 수산화칼슘(Ca)이 혼입된 조건에서 최대강도가 확인되었다. 7일후 이어치기 압축강도 측정결과 나노슬래그(N.S)에 알칼리자극제(Na, Ca, Ka)를 단독으로 사용하는 것만으로 는 강성증가가 적었으며, 복합사용 조건에서는 재령 7일 전 조건에서 OPC와 유사 또는 상회하는 결과가 확인되었 다.7일후 이어치기 휨강도 측정결과 재령 3일에서 나노슬래그(N.S)와 수산화칼슘(Ca)을 사용한 조건에서 최대 강 도가 관찰되었으며, 재령 7일의 복합사용 조건에서는 OPC를 최대 14%이상 상회하는 높은 강도 증진이 확인되었 으나, 재령 28일에서는 유사한 것으로 측정되었다.