earticle

영어

This research developed ultra-pressure pump main body by using ductile cast iron FCD500, conducted quantitative analysis on following phenomenon of flow or solidification processing in cast processing for improvement of cast device, after extracting model from cast concluded as follows by brinel hardness test. after selecting the ideal condition of cast and it applied to cast of real product shape, discovered the ideal filling processing under the condition that temperature of molten metal was between 1300℃ and 1280℃. and after finishing filling, solidification was commenced rapidly when percentage of solidification completion was between 40%~50%, at that moment, the termperature was measured 1100℃. moreover under the condition of temperature below 900℃, keeping temperature on the center of parts for a certain period of time brings stability of stabilization of heat in parts and organizational stabilization of ductile cast iron. As the results of the casting method design, it was that the ductile cast parts of pump main body was obtained as the maximum HB of 220 was recorded and good test results were achieved