earticle

영어

This study investigated the efficient and specific procedures and principles of metal type wax casting method with an improved experiment. (1) The matrix material: Beeswax and injection wax were useful as the material. (2) The mould material: Yellow earth was useful as the filling material. Paper fiber, rice straw, activated carbon, oil carbon, graphite and water carbon, among others, were useful as the functional material. The mixture proportion was 0.5∼2% for paper fiber, 1% for rice straw, 5∼18% for activated carbon, 5% for oil carbon, 5 % for graphite and 5∼5.5% for water carbon, respectively. In particular, paper fiber played a critical role in preventing cracks in the mould, and rice straw was also found to have the similar function. (3) The metal components, pouring quantity, and pouring method: Bronze was effective as the metal component. A small quantity of approximately 300∼350 grams was poured using conventional method. (4) The number of character strokes: The fewer the number of character strokes, the higher the success rate was. However, the variance of success rate was only 15.62%. (5) The pouring direction of metal fluid: When putting the character face in the lateral direction and pouring metal fluid in a standing manner, it resulted in 74.0% success rate. (6) The main path caliber for metal fluid: The size of 4.5 × 5.0㎜ was sufficient. The length of 190㎜ was effective. In particular, the length of the main path caliber was the critical factor in the success rate by increasing the pouring pressure of metal fluid. (7) The temperature of mould: The temperature of 600℃ was sufficient as the burning temperature for mould. The mould temperature when pouring metal fluid had little effect on the success rate. (8) The casting success rate and contraction rate: The highest success rate was 100%, and the overall success rate was 74.0%. The contraction rate was 2.69%. (9) The characteristics and performance of type strokes: All the distinctive characteristics in Jikji were observed here. The overall type performance was very high not only in the measurable aspects, but also in the similarity of the writing type which cannot be quantified. Therefore, it is highly probable that the wax casting method employed by this experiment is the replication of the method actually used to cast Jikji type.

한국어

금속활자를 주조할 수 있는 밀랍주조법의 개량 실험을 통하여 효율적이고 구체적인 과정과 원리 를 추적하였다. (1) 어미자의 재료: 밀랍과 함께 왁스가 효과적이었다. (2) 주형의 재료: 충전 재료로 황토는 유용하였다. 기능성 재료로 종이 섬유․볏짚․활성탄․유성 탄소․흑연․수성 탄소 등은 유용하였다. 그 혼합 비율은 종이 섬유는 0.5∼2%, 볏짚은 1%, 활성탄은 5∼18%, 유성 탄소는 5%, 흑연은 5%, 수성 탄소는 5∼5.5%였다. 특히 종이 섬유는 주형의 균열을 방지하는 기능이 절대적일만큼 탁월하였고, 기타의 기능성 재료 비율이 높을수 록 종이 섬유의 비율도 높아야 했다. 볏짚은 종이 섬유와 같은 기능이 있음을 확인하였다. (3) 금속의 재료 및 주입 양과 방법: 청동은 효과적이었다. 주입 양은 300∼350g 정도의 소량을 재래식 방법으로도 주입할 수 있었다. (4) 문자 필획의 다과: 필획이 적을수록 성공률이 높기는 했으나, 그 편차는 15.62%에 불과하였다. (5) 금속 용액의 주입 방향: 문자면을 측향으로 하여 금속 용액을 입식으로 주입한 결과 74.0%의 성공률을 나타냈다. (6) 주탕도의 굵기와 길이: 4.5 × 5.0㎜ 굵기의 주탕도로도 충분하였다. 길이는 190㎜가 효과적이 었다. 특히 주탕도의 길이는 금속 용액의 주입 압력을 높여서 성공률에 절대적인 영향을 미 쳤다. (7) 주형의 온도: 주형의 소성 온도는 600℃로도 충분하였다. 금속 용액 주입 시 주형의 온도는 성공률과 무관하였다. (8) 주조의 성공률과 수축률: 최고의 성공률은 100%였고, 전체의 성공률은 74.0%였다. 수축률은 2.69%였다. (9) 활자 자적의 특징과 완성도: ｢직지｣에서 발견할 수 있는 특징이 모두 나타났다. 활자의 완성 도는 수치로 표현할 수 있는 요소는 물론, 수치로 표현할 수 없는 필서체 자형의 유사도까지 매우 높았 다. 따라서 본 연구가 제시한 밀랍주조법은 직지활자를 주조하기 위하여 사용했던 방법일 가능성이 높은 것으로 보인다.