Pyroporcessing of spent nuclear fuel generates a considerable amount of LiCl-KCl eutectic waste salt containingradioactive rare earth (RE) chlorides. In this study, a series of processes, which consist of a phosphorylation/distillationprocess and a solidification process, were performed to minimize volume of the LiCl-KCl eutectic wastesalt and solidify a residual waste into a stable form at a relatively low temperature. Over 99wt% of RE chlorides inLiCl-KCl eutectic salt was converted and separated into REPO4 in the phosphorylation/distillation process usinga mixture of Li3PO4-K3PO4. The separated REPO4 was solidified into a homogeneous and fine-grained form at1,050℃ using LIP(Lead Iron Phosphate) as a solidification agent. The final waste volume was reduced below about10% through the series of the processes.

한국어

사용후핵연료 파이로프로세싱에서 발생하는 LiCl-KCl 공융염폐기물의 부피를 최소화하고 최종적으로 잔류하는 폐기물을비교적 낮은 온도에서 안정한 형태로 고화하고자 희토류 핵종 염화물을 함유한 LiCl-KCl 공융염을 이용하여 인산화/증류 및세라믹 고화의 일련공정을 수행하였다. LiCl-KCl 공융염 내 희토류 염화물은 혼합인산화제(Li3PO -K3PO4)를 이용한 인산화및 공융염 감압증류공정을 통하여 99% 이상을 인산화물 형태로 전환/분리할 수 있었고, 분리한 희토류 인산화물은 고화매질로서 LIP(Lead Iron Phosphate)를 이용하여 1,050℃에서 균질하고 치밀한 형태의 고화체로 제조할 수 있었으며, 최종적으로 발생하는 방사성 폐기물 부피를 10% 이하로 감용할 수 있음을 확인하였다.