To reduce the magnetization loss of a coated conductor, the striation and the transposition have to be accomplished for magnetic decoupling. The loss reduction effect in incomplete as well as complete striated YBCO CCs was reported in previous research. At the case of the incomplete striated sample, the end region of the sample is non-striated. So, it is not jointed with each other. In power applications, the joint is needed because current leads must be connected with HTS coils. In this research, the influence of end-joint methods with copper and superconducting joint on magnetization loss in striated YBCO CC and spiral winding samples are presented and compared with non-striated measured result.
목차
Abstract
1. INTRODUCTION
2. SAMPLES AND EXPERIMENT
2.1. Samples for angular dependency in helical
2.2. Samples for end-joint effect of magnetization loss
2.3. Experimental set-up
3. RESULTS AND DISCUSSION
3.1. Results of angular dependency in helical
3.2. Samples for end-joint effect of magnetization loss
4. CONCLUSION
ACKNOWLEDGMENT
REFERENCES
1. INTRODUCTION
2. SAMPLES AND EXPERIMENT
2.1. Samples for angular dependency in helical
2.2. Samples for end-joint effect of magnetization loss
2.3. Experimental set-up
3. RESULTS AND DISCUSSION
3.1. Results of angular dependency in helical
3.2. Samples for end-joint effect of magnetization loss
4. CONCLUSION
ACKNOWLEDGMENT
REFERENCES
저자정보
참고문헌
자료제공 : 네이버학술정보