금속-도재관용 Ni-Cr합금의 조성변화와 소성단계에 따른 전단결합강도

원문정보

Observation of Shear Bonding Strength by Compositional Change and Firing Steps of the Ni-Cr Alloy for Porcelain Fused Metal Crown

조용완, 홍민호, 김원영, 최성민, 정인성

피인용수 : 0(자료제공 : 네이버학술정보)

초록

영어

Purpose: This study was observation shear bonding strength by compositional change and firing step of a Ni-Cralloy for porcelain fused metal crown. The aim of study was to suggest the material for firing step of Ni71-Cr14alloy to development of alloy for porcelain fused to metal crown. Methods: The test was on the two kinds of Ni-Cr alloy specimens. The surfaces of two alloys were analyzed byEDX in order to observe oxide characteristic. And the shear test was performed by MTS. Results: The surface property and oxide characteristic analysis of oxide layer, weight percentage of Element Owithin Ni71Cr14 alloy measured 23.32wt%, and Ni59Cr24 alloy was measured 23.03wt%. And the maximum shearbonding strength was measured 58.02 between Ni59Cr24 alloy and vintage halo(H4 group). Conclusion: The surface property and oxide characteristic three kind of Ni-Cr alloy was similar. and shearbonding strength showed the highest bonding strength in H4 specimens.

목차

[Abstract]
 Ⅰ. 서론
 Ⅱ. 연구 방법
  1. 실험 재료
  2. 시편 제작
  3. 실험 방법
 Ⅲ. 결과
  1. 전단결합강도
  2. 표면성분관찰
 Ⅳ. 고찰
 Ⅴ. 결론
 REFERENCES

저자정보

  • 조용완 Yong-wan Cho. 부산가톨릭대학교 보건과학대학 치기공학과
  • 홍민호 Min-ho Hong. 부산가톨릭대학교 보건과학대학 치기공학과
  • 김원영 Won-young Kim. 부산가톨릭대학교 보건과학대학 치기공학과
  • 최성민 Sung-min Choi. 부산가톨릭대학교 보건과학대학 치기공학과
  • 정인성 In-Sung Chung. 부산가톨릭대학교 보건과학대학 치기공학과

참고문헌

자료제공 : 네이버학술정보

    함께 이용한 논문

      ※ 기관로그인 시 무료 이용이 가능합니다.

      • 4,000원

      0개의 논문이 장바구니에 담겼습니다.