This paper study on the basic properties of mortar using red clay. Red clay has been used as a traditional architectural material. In these days, red clay is often used for plastering in newly constructed buildings to minimize sick building syndrome. But the reactivity of red clay is low, the replacement ratio of non-sintering red clay was higher for mortar. They had many cracks. So it is very hard to use building material. In this reason, we analysis red clay boiled low temperature. The specimens were made of boiled red clay with various mixing ratio(5, 10, 15, 20, 25, 30, 35, 40, 45, 50%). As a results, when mixing ratio of boiled red clay was increased from 0% to 50%, it was observed that mortar flow are in rapid decline. However, the mixing ratio of boiled red clay was increased from 0% to 40%, it was observed that compressive and bending strength of mortar was increased. Observing of total crack numbers, all specimens showed that as mixing rates of boiled red clay were increased as crack numbers were increased.

한국어

본 연구는 가수가열가공 황토를 사용한 모르타르의 기초적 특성에 대하여 연구하였다. 황토는 오랜기간 전통적 건축재료로서 사용되어 왔다. 현재에 황토는 새집증후근을 최소화하기 위하여 새로운 건축 미장재로 사용되고 있다. 그러나 황토의 반응성이 매우낮아 비소성한 황토의 대체율이 증가할수록 많은 균열이 발생한다. 따라서 건설 재료로서 사용하기는 매우어렵다. 이러한 이유로 본연구에서는 저온으로 가수소성한 황토에 대하여 분석하였다. 가수가열가공 황토의 대체율을 5~50%까지 다양하게 만들었다. 결과로서 모르타르에서 가수가열가공 황토의 대체율이 증가할수록 모르타르 플로우는 급격히 감소하였다. 그러나 가수가열가공 황토의 대체율이 40%까지 증가하였을 때, 압축강도와 휨강도가 증가하였다. 총균열 발생수를 확인한 결과 모든 공시체에서 가수가열가공 황토의 대체율이 증가할수록 균열 수는 증가하였다.