earticle

영어

This study intends to identify properties of setting and hardening for concrete using high early strength AE water reducing agent. Early strength method of concrete is classified into few categories such as using ultra high strength cement and promoting compound or high early strength AE water reducing agent. However ultra high strength cement or promoting compound have difficulties being applied on site due to higher economy and slump loss. Therefore, this study use high early strength AE water reducing agent. The results of experimentation are as follow. When adding high early strength AE water reducing agent, that cut cement setting time down to under 30~60 minutes in initial setting time and to under 30~120 minutes in final setting time. A Slump of concrete adding high early strength AE water reducing agent measured 15.5~16.5cm and using high early strength AE water reducing agent tend to increase slump with adding ratio. When adding ratio of high early strength AE water reducing agent in concrete was increased from 0% to 1.5%, it was observed that compressive strength of concrete measured from 35 to 41.73MPa. And when adding high early strength AE water reducing agent, test result showed that crack numbers is less than plain concrete's crack numbers.

한국어

본 연구에서는 조강형 AE감수제를 사용한 콘크리트에 대한 경화 및 응결특성에 대하여 알아보았다. 콘크리트 조기강도를 확보하는 방법은 초조강시멘트나 촉진제 또는 조강형 AE감수제를 사용하는 방법이 있다. 그러나 초조강시멘트나 촉진제는 높은 경제성과 유동성 손실 때문에 현장에 적용하기 어려운 점이 있다. 따라서 본 연구에서는 조강형 AE감수제를 사용하고자 한다. 실험결과 조강형 AE감수제를 사용하였을 때 초결이 30~60분 단축되었으며, 종결이 30~120분 단축되었다. 그리고 슬럼프 값은 15.5~16.5cm로 측정되었다. 그리고 조강형 AE 감수제의 혼입량이 0~1.5%까지 증가하였을 때 압축강도는 35~41.73MPa를 나타내었다. 또한 균열발생량이 기본시편에 비하여 적게 나타난 것을 알 수 있었다.