The electrochemical behaviors of 10 g-scale fresh and oxidized Zircaloy-4 cladding hulls were examined in 500oC LiCl-KCl molten salts to confirm the feasibility of the electrorefining process for the treatment of hull wastes. In the results of measuring the potential-current response using a stainless steel basket filled with oxidized Zircaloy-4 hull specimens, the oxidation peak of Zr appears to be at -0.7 to -0.8 V vs. Ag/AgCl, which is similar to that of fresh Zircaloy-4 hulls, while the oxidation current is found to be much smaller than that of fresh Zircaloy-4 hulls. These results are congruent with the outcome of current-time curves at -0.78 V and of measuring the change in the average weight and thickness after the electrochemical dissolution process. Although the oxide layer on the surface affects the uniformity and rate of dissolution by decreasing the conductivity of Zircaloy-4 hulls, electrochemical dissolution is considered to occur owing to the defect of the surface and phase properties of the Zr oxide layer.

한국어

전해정련을 이용한 폐 피복관 처리의 타당성을 살펴보기 위하여, 500℃의 LiCl-KCl 용융염 내에서 표면이 산화된 10 g 규모의Zircaloy-4 피복관 및 순수한 Zircaloy-4 피복관의 전기화학적 거동을 살펴보았다. 산화된 Zircaloy-4 피복관이 담긴 basket을 작업전극으로하여 전압-전류 관계를 측정한 결과, 산화되지 않은 Zircaloy-4 피복관과 비교해 Zr의 산화 peak는 Ag/AgCl 기준전극 대비, 약 -0.7 V ~ -0.8 V로 유사한 반면, 산화 전류의 크기는 확연하게 감소하는 것으로 나타난다. 이러한 결과는 -0.78V의 일정전위를 가한 전기화학적 용해 실험에서 살펴본 전류-시간 곡선에서도 유사하게 나타나며, 피복관 조각들의 평균 두께 및 무게 변화로부터 확인할 수 있다. Zircaloy-4 피복관이 산화되었을 경우, 표면의 산화막이 피복관의 전도성에 영향을 주어 basket 내 위치에 따라 전기화학적 용해의 균일성 및 속도를 떨어뜨리는 것으로 나타나지만, 표면의 미세한 결함과 Zr 산화물의 상 특성으로 인해 전기화학적 용해가 진행되는 것으로 판단된다.