In this study, Made Ag powder that efficiency is to various material to make latent fingerprint detection powder in various size and type (rod 2 kinds, flake 2 kinds, spherical 1 kind) by liquid reduction method. Examined about particle size and topology get manufacture Ag powder and commercial silver powder, magnetic powder to latent fingerprint detection efficiency after detection on glass, plastic, leather. Flake type showed similar to commercial silver powder glass and plastic, experiment result non-porous surface, and 0.9 μm Ag I powder of rod type and 10~20 μm Ag II powder showed than commercial silver powder that efficiency detection is augmented. Also, optimized detection is high enough to Ag I (rod, 0.9 μm) powder and Ag II (rod, 10~20 μm) powder confirm fingerprint ridge on naked eye in leather and Ag II (rod, 10~20 μm) powdered detection efficiency is superior by contrast effect with material of black order.

한국어

잠재지문 현출용 분말을 제조하기 위해 다양한 대상물질에 효율성이 있는 Ag 분말을 액상환원법으로 다양한 크기와 형태(rod 2종류, flake 2종류, spherical 1종류)로 제조하였다. 제조 Ag 분말과 시판중인 흰색계열 silver 분말, magnetic 분말을 유리, 플라스틱, 가죽에서 현출 후 입자크기와 형태가 잠재지문 현출효율에 미치는 영향에 대하여 실험하였다. 비다공성 표면인 유리와 플라스틱에서는 flake 형태는 시판 silver 분말과 유사한 현출결과를 보였고, rod 형태의 0.9 μm Ag I분말과 10~20 μm Ag II분말은현재 시판중인 silver 분말보다 현출효율이 증대됨을 보여주었다. 가죽에서는 Ag I (rod, 0.9 μm) 분말과Ag II (rod, 10~20 μm) 분말이 마그네틱 분말에 비해 높은 현출효율을 보였으며 검은색계열의 대상물질과의 대비효과로 Ag II (rod, 10~20 μm) 분말의 현출효율이 우수함을 알 수 있었다.