The purpose of this study is to investigate the compressive strength property of Ground Blast-Furnace Slag(GBFS) using water eluted from recycled coarse aggregate. When GBFS come into contact with water, they have not a autonomously chemical reaction. But GBFS is a latent hydraulic property when GBFS come into contact with water in alkaline environment. For that reason, if water eluted from recycled coarse aggregate use mixture water, GBFS is expected to reaction of latent hydraulic property in early stage. Therefore we conducted an tests of XRD, ICP-MS, Compressive Strength, after the mortar make form water eluted from recycled coarse aggregate. And then it is to investigate the effect of the hydration properties of GBFS using water eluted from recycled coarse aggregate. According to the experimentation result, ICP-MS analysis showed water eluted from recycled coarse aggregate has a high alkali-ash value of PH of 12 and over. And GBFS mortar using water eluted from recycled coarse aggregate showed a similar strength of plain mortar due to the latent hydraulic reaction. XRD analysis showed GBFS mortar using water eluted from recycled coarse aggregate have significantly decreased presence of calcium hydroxide.

한국어

본 연구의 목적은 순환굵은골재로부터 용출시킨 물을 사용하여 고로슬래그 미분말의 압축강도 특성에 관하여 조사하는 연구이다. 고로슬래그 미분말은 자체적으로는 물과 접촉하게 되면 반응성이 없으나, 고알칼리 환경 하에서는 자체적으로 물과 접촉하였을 때 잠재수경성 반응을 일으키는 재료이다. 그렇기 때문에 순환굵은골재에 물에 담궈 용출된 고알칼리수를 배합수로 사용하게 되면 고로슬래그 미분말의 잠재수경성 반응을 조기에 일으킬 것으로 예상된다. 따라서 본 연구에서는 순환골재로부터 용출시킨 물을 배합수로 사용한후 모르터를 제조하여, XRD, ICP-MS, 압축강도를 측정하여 용출수가 고로슬래그 시멘트 수화물의 성상에 미치는 영향을 종합적으로 분석하고자 하였다. 실험결과 ICP-MS 분석에서 순환굵은굵은골재로부터 용출시킨 물에 PH12이상의 알칼리 성분이 나타났다. 그리고 잠재수경성 반응으로 인하여 순환굵은골재로부터 용출시킨 물을 사용한 고로슬래그 미분말 모르타르가 플레인과 동일한 압축강도를 나타내었다. XRD분석결과 순환굵은골재로부터 용출시킨 물을 사용한 고로슬래그 미분말 모르타르의 수산화 칼슘이 소비된것을 알 수 있었다.