This study aims to investigate nitrate and phosphate removal using alumina cement (UAC50) and Ca (OH)2. The study included the following reaction parameters for the removal of nitrate removal: reaction time, UAC50 addition, Ca (OH)2 addition and the ratio of UAC50/Ca (OH)2. FE-SEM and EADX analysis are also used to find out microstructure of precipitate and chemical composition of the precipitate. The precipitate was revealed to be calcium-nitro-aluminate according to EDAX result. Maximum removal of nitrate was shown at 80 min reaction time. Addition of UAC50 or Ca (OH)2 solely did not remove nitrate effectively. UAC50 and Ca (OH)2 should be added together in the wasteater to remove nitrate ion effectively. The optimum ratio of UAC50/Ca (OH)2 was 2.2 to remove the nitrate and the removal ratio was 46%. Phosphate was not removed by sole UAC50 addition and sole Ca (OH)2 addition showed 46 and UAC50 and Ca(OH)2 addition showed 47% phosphate removal.

한국어

본 연구에서는 알루미나 시멘트인 UAC50과 Ca(OH)2를 이용하여 질산성 질소와 인의 제거특성을 조사하는 것을 목적으로 반응시간, UAC50 주입율, Ca(OH)2 주입율, 그리고UAC50/Ca(OH)2 질량비에 따른 질산성 질소의 제거 특성을 조사하였고 FE-SEM과 EDAX를 통해서 공시료와 응집반응 후 침전물의 미세구조 및 구성성분비를 조사함으로써 질산성질소가 Calcium-nitro-aluminate형태로 제거되는지를 확인하였다. 응집 반응시간은 80분에서 질산성질소의 최대제거효율이 나타났고 UAC50 단독주입 혹은 Ca(OH)2 단독주입 시 질산성 질소 제거율은 크지 않았다. UAC50과 Ca(OH)2 동시 주입 시 질산성 질소 제거가 효율적으로 이루어졌으며 UAC50/Ca(OH)2 질량비 2.2에서 46% 질산성 질소 제거특성을 나타내었다. 인산이온은 UAC50 단독주입시 제거되지 않았고 Ca(OH)2 단독주입이나 Ca(OH)2와 UAC50 동시 주입 모두 46% 정도의 제거율을 나타내었다.