This paper investigates the applicability of hydration heat reducing method of mass concrete structure for mat foundation studied by the authors to achieve volumetric stability and economical profit. Hydration heat reducing method developed by the authors reflects the difference of produced heat during hydration period between placing layers. Adiabatic Temperature Rising Test and mock-up test are carried out varying with mixture proportion. According to results, function is applied to estimate hydration heat development with age. By computing the function above, maximum temperature rise and the time to initiate heat production are clarified with different mixture proportion more accurately. Mock-up specimen C has lower maximum temperature than specimen A by as much as 7.5℃. As top section concrete begins to produce a heat earlier than bottom section concrete, occurrence of thermal crack induced by tensile stress at surface can be avoided. For compressive strength, the mixture combination of S-F30, R-F30, which incorporate fly ash exhibits a reduction in compressive strength by as much as 5～10 MPa compared with other mixture combination at 28days. There's no remarkable difference of strength development with and without fly ash based on the results of core test.

한국어

본 연구에서는 건축물 매트기초 매스콘크리트의 수화열 저감 및 경제성 성취에 활용될 수 있도록 배합종류 변화에 따른 단열온도상승특성과 모의부재 실험을 통하여 적용가능성에 대하여 검토하고자 하였다. 실험 결과에 따르면 먼저, 단열온도상승 특성으로 배합 종류에 따라 단열온도상승식을 근사식 을 검토하여 결정계수(R2) 0.994이상이 되는 식을 얻을 수 있었으며, 각 배합에 따라 최고 온도상승량과 수화반응에 의한 발열시점을 보다 정확히 확인 할 수 있었다. 모의부재의 수화열 온도이력 특성으로 모의부재 C의 경우 모의부재 A와 비교 하여, 최고온도는 약 7.5℃ 저감 시켰다. 또한 상부콘크리트가 먼저 수화발열함으로서 표면부의 인장응력에 대한 온도균열을 제어 할 수 있는 것으로 나타났다. 압축강도 특성으로 배합종류별 표준양생공시체의 경우 플라이애시를 치환한 S-F30, R-F30콘크리트는 치환하지 않은 S-P, E-P콘크리트 보다 압축강도가 약 5～10MPa정도 재령 28에서 저하된 것으로 나타났으나, 코어압축강도의 경우에서는 플라이애시 치환사용에 따른 차이가 없는 것으로 분석되었다.