Accordingly architectural structure is getting high-rise and bigger, a use of high strength and high performance concrete has been increasing. High performance concrete has cons of explosion in a fire. This Explosion in the fire can cause the loss of the sheath on a concrete surface, therefore it effects that increasing a rate of heat transmission between the steel bar and inner concrete. Preventing this explosion of high performance concrete in the fire, many kinds of researches are now in progressing. Typically, researches with using Polypropylene-fiber and Steel-fiber can prove controling the explosion, but the reduction of mobility was posed as a problem of workability. Consequently, to solve the problem as mentioned above, concrete cans secure fire resisting capacity through the using of coating liquid, including Ester-lubricant and non-ionic characteristic surfactant. This research has been drawn a ideal condition in compressive strength areas of concrete by an experiment. When applying 13mm of polyamide-fiber, proper fiber mixing volume by compressive strength areas of concrete is 0.8kg/m3 in 60MPa, 1.0kg/m3 in 80MPa, 1.5kg/m3 in 100MPa/m3. These amount of a compound can control the explosion.

한국어

최근 건축구조물에 있어서 초고층화, 대형화의 요구에 의해 고강도 및 고성능 콘크리트의 사용이 증가하고 있다. 하지만 고강도 및 고성능 콘크리트는 화재 시 발생하는 폭렬현상에 취약한 문제가 있다. 폭렬은 화재 시 콘크리트 피복의 손실을 초래하여 내부콘크리트와 철근의 열전달률을 높여 콘크리트와 철근의 온도를 상승시키는 작용을 한다. 이러한 고강도 콘크리트의 화재 시 폭렬을 방지하기 위하여 많은 연구들이 진행되고 있으며, 대표적으로 폴리프로필렌(polypropylene)섬유, 강섬유를 콘크리트에 혼입한 연구들에 의해 폭렬제어성능이 입증되었으나, 섬유 혼입에 따른 유동성 저하 및 시공성 불량 등의 문제점이 제기되고 있다. 따라서 본 연구에서는 이와 같은 문제를 해결하기 위하여 에스테르계 윤활제 및 비이온성 계면활성제를 포함한 코팅액으로 코팅된 Polyamide 섬유를 콘크리트에 혼입하여 내화성능 및 시공성을 확보하였으며, 강도영역별 적정 조건을 실험을 통하여 도출하였다. 그 결과, 13mm의 polyamide 섬유 적용시 강도영역별로 60MPa에서는 0.8kg/m3, 80MPa에서는 1.0kg/m3, 100MPa는 1.5kg/m3이상 혼입시 폭렬 제어 및 시공성 확보가 가능할 것으로 사료된다.