This study aimed at improving the TiO2 photocatalytic degradation of humic acid. In this study, the degradation of HA using Jeju scoria coated with WO3/TiO2 in the presence of UV irradiation was investigated as a function of different experimental condition : photocatalyst dosage, Ca2+ and HCO3 − addition and pH of the solution. Photodegradation efficiency increased with increasing photocatalyst dosage, the optimum catalyst dosage is 2.5 g/L and photodegradation efficiency is maximized to WO3/TiO2 = 3/7. This indicates that WO3 retains a much higher Lewis surface acidity than TiO2 and WO3 has a higher affinity for chemical species having unpaired electrons. The addtion of cation (Ca2+) in water increased the photodegradaion efficiency. But the addtion of HCO3 − ion in water decreased a photodegradation efficiency. Photodegradation efficiency increased with decreasing pH. At pH < pzc, the electrostatic repulsion between the HA and the surface of TiO2 decreased.

한국어

본 연구에서는 제주산 스코리아에 TiO2, WO3/TiO2 광촉매를 코팅하여 다 양한 반응영향 인자에 따른 휴믹산(HA)의 분 해효율을 검토하였다. 여기에서 광촉매량에 따른 휴믹산의 분해효율을 비 교해 볼 때 경제적인 측면에서의 투여량은 2.5 g/L이 적정하다고 판단되었다. 그리고 각 촉매의 분해효율을 보면 WO3/TiO2 (3/7)에서 효율이 가장 높았다. 또한 휴믹산 의 분해시 수중에 Ca2+를 첨가하였을 때가 효율은 증가하였지만 HCO3 − 경우는 Ca2+와 반대의 경향을 보였다. 한편, 초 기 pH에 따른 휴믹산의 분해효율을 검토한 결과 초기 pH 4일 때가 pH 10일 때보다 분해효율은 높았는데 이것은 pH가 TiO2의 pzc 이하에서 TiO2와 휴믹산 분자사이의 정전기적 인력이 증가하 여 효율이 증가한 것으로 판단된다.