Scale Formation Test with Various Pipe Materials for Pipeline Scale Management
초록
영어
The scales induced by hardness materials and corrosion products in water need to be controlled, because they can inhibit the function of pipeline and deteriorate water quality, finally result in huge losses. Especially in hot water system, scales can be accelerated by high temperature. Three kinds of pipe coupon were submerged in test water having 500 mg/L of hardness at 80oC and the most scale was formed on cast iron pipe (CIP) coupon followed by copper (CU) and stainless steel (SUS). From the results of SEM and XRD, scale was producted by corrosion materials from pipe and Ca hardness in water. Carbonic acid caused by corrosion reaction induced Ca precipitation. Scale mass and corrosion rate was measured through weight loss of coupons after immersing time and CIP showed highest scale mass and corrosion rate.
한국어
수중 경도물질에 의해 유발된 스케일은 수질 저해는 물론 배관의 기능에 막대한 손실을 초래할 수 있어 관리가 필요하 다. 특히 온수시스템의 경우, 온도에 의해 스케일화작용이 가속화되므로 관리가 필요한 시설 중 하나이다. 500 mg/L의 경 수에 대한 관 재질별 스케일 형성 특성 비교 실험 결과, 주철관(CIP) 시편에 서의 스케일 형성도가 매우 컸으며, 다음으로 구리(CU), 스테인리스스틸관(SUS)의 순이었다. 스케일량과 부식율 분석은 관종별 시편을 일정기간 침지시킨 후의 무게 를 측정하여 스케일량은 무게증가량으로 부식율은 무게감소량으로 CIP 48.79 mdd, Cu 19.39 mdd 및 SUS 2.86 mdd이 였고, CIP의 부식속도가 가장 큰 것으로 나타났다.
목차
요약문
I. 서론
II. 연구방법
1. 경수의 스케일 형성 특성
2. 분석항목 및 방법
III. 연구결과
1. 국내외 관내 스케일 제어 방안
2. 관 재질별 스케일 형성 특성
IV. 결론
References