Grindability of Cast Ti-X%Zr(X=10,20,40) Alloys for Dental Applications
초록
영어
Purpose: The grindability of binary Ti-X%Zr(X=10,20,40) alloys in order to develop a Ti alloy with better machinability than unalloyed titanium has been evaluated. Methods: Experimental Ti-Zr alloys were made in an argon-arc melting furnace. Slabs of experimental alloys were ground using a SiC abrasive wheel on an electric handpiece at circumferential speeds(12000,18000,25000 or 30000rpm) by applying a force(200gr). Grinding rate was evaluated by measuring the amount of metal volume removed after grinding for 1 minute and the volume ratio of metal removed compared to the wheel material lost, which was calculated from the diameter loss (grinding ratio). Experimental datas were compared to those for cp Ti(commercially pure titanium) and Ti-6%Al-4%V alloy were used controls. Results: It was observed that the grindability of Ti-Zr alloys increased with an increase in the Zr concentration. More, they are higher than cp Ti, particularly the Ti-20%Zr alloy exhibited the highest grindability at all circumferential speeds. There was significant difference in the grinding rate and grinding ratio between Ti-20%Zr alloy and cp Ti at any speed(p<0.05). Conclusion: By alloying with Zr, the Ti exhibited better grindability at all circumferential speeds. the Ti-20%Zr alloy has a great potential for use as a dental machining alloy.
목차
Ⅰ. 서론
Ⅱ. 연구 방법
1. 시료의 설계
2. 시료 제조
3. 연삭 시험
4. 시료의 EDS 분석 및 연삭 chip, 연삭면의 SEM 관찰
Ⅲ. 결과
1. 연삭성
2. 연삭 chip 및 연삭면의 SEM 관찰
Ⅳ. 고찰
1. 연삭성
2. 연삭 chip 및 연삭면의 SEM 관찰
참고문헌