Flowing and Strength properties of the Ternary Low-carbon Inorganic Composites Depending to Reinforced PVA Fiber
초록
영어
The purpose of the study reduced environmental load and CO2 gas, when the cement was produced, using cement substitutes. It was consisted of blast furnace slag, red mud and silica fume which were industrial byproduct. PVA fiber was set to 5 levels of 0, 0.5, 1, 1.5, 2(%) ect in the low carbon inorganic Composites drawn in the advanced research. The ring floor, setting time, compressive strength, and flexural strength were set to the measure and the experiment was carried out. The experiment was carried out, The liquidity was more and more reduced as the percentage of Reinforced of PVA fiber increased. However this difference indicated the tendency that it represents the slight tendency and the final setting time is reduced in the flocculation test. In the strength test, the compressive strength was lower than Plain with the age on 1st in case of Reinforced PVA fiber. The age showed the compressive strength more than 50MPa From 3 day of agerd. And the flexural strength showed excellently as PVA percentage of dilution increased.
목차
1. 서론
1.1 연구의 배경
1.2 연구의 목적
2. 사용재료
2.1 고로슬래그(Blast Furnace Slag)
2.2 레드머드(Red Mud)
2..3 실리카 흄(Red Mud)
2.4 알칼리 자극제
3. 기초실험계획 및 분석
4. 선행실험계획 및 결과
4.1 선행실험계획
4.2 선행실험 분석
5. 본 실험계획 및 방법
5.1 실험계획
5.2 실험방법
6. 실험결과 및 분석
6.1 유동성 및 응결시험 분석
6.2 압축 및 휨강도 시험
7. 결론
참고문헌