The objectives of this experimental research were to investigate the diffusion characteristics for chloride ion of concrete subjected to sulfate attack and suggest high-resistance concrete against sulfate attack and chloride penetration. For this purpose, concretes with three types of cement such as ordinary portland cement (OPC), binary blended cement (BBC), and ternary blended cement (TBC) containing mineral admixtures were made for water-binder ratios of 32% and 43%. After the concrete specimens were immersed in sulfate solution for 365 days, mass change ratios of them were measured, and then the resistance against chloride ion penetration of them were estimated by using NT BUILD 492. It was observed from the test results that the resistance to chloride ion penetration of concrete subjected to sulfate attack was greatly decreased than that of standard curing concrete under the same age. Also, it was revealed that the resistance to chloride ion penetration of concretes containing mineral admixtures such as BBC and TBC were much better than that of OPC concrete.

한국어

황산염 침투 및 염해환경에 노출된 철근 콘크리트 구조물의 경우 콘크리트의 팽창균열 및 철근부식으로 인하여 내구 수명이 단축되면 기설 구조물의 보강이나 재설치가 시행되는데, 이 때 기설 구조물의 폐콘크리트 처리 문제로 환경부하가 증가하게 된다. 따라서 황산염 침투 및 염해로 인한 환경부하를 저감하기 위해서는 황산염 침투를 받은 콘크리트의 염화물이온 침투 저항성을 정확히 예측하여 설계·시공하여야 한다. 본 연구의 목적은 황산염 침투를 받은 콘크리트의 염화물이온 침투 저항성을 규명하여 황산염 침투 및 염해 고저항성 콘크리트를 제시하는 것이다. 이를 위하여, OPC, 2성분계 및 3성분계 시멘트를 혼입한 3가지 형태의 콘크리트를 물-결합재비 32% 및 43%에 대해서 제작하였다. 제작한 콘크리트 시험체를 365일 동안 황산염 용액에 침지시킨 후 그것의 질량 변화율을 평가하였고, NT BUILD 492에 의해 염화물이온 침투 저항성 시험을 수행하였다. 그 결과, 황산염 침투를 받은 콘크리트는 동일 재령의 표준양생 콘크리트보다 염화물이온 침투 저항성이 크게 저하되는 것으로 나타났으며, 광물질 혼화재를 혼입한 2성분계 및 3성분계 시멘트를 사용한 콘크리트의 염화물이온 침투 저항성은 OPC 콘크리트의 경우보다 훨씬 우수한 것으로 나타났다.