A Study on Shear Bond Strength of Heat Press Ceramic to Non Precious Porcelain Metal
초록
영어
Purpose: Heat pressed ceramics, used for all ceramic restorations, have the additional advantage of being technically less change through using of the lost-wax technique. Conceptually, combining the ceramic with the clinically proven reinforcing ability of a metal framework would be advantageous; however, cause of mismatching of fusion between ceramics and metal frameworks which from differences of casting temperature and coefficient of thermal expansion, pressed ceramics could not be used with a metal framework. The purpose of this study was to compare shear bond strength of press-to metal ceramic to porcelain fused non precious metal and feldspatic porcelain fused non precious metal.
Methods: The 30 metal specimens were casted in a porcelain fused non precious metal nickel-chromium alloy.
They were divided into 3 groups by surface treatment and applied ceramic: 125 aluminium oxide sandblasting and veneered feldspatic porcelain (group FP), 125 aluminium oxide sandblasting and had press-to-metal ceramic applied (group PC), porcelain bonder (gold bonder) fused on surface of metal specimens and had press-to-metal ceramic applied (group PCG). In each group 10 metal specimens were used. The press-to-metal ceramic applied 20 specimens had ash-free wax pattern applied, the metal-wax complexes invested, and were pressed with heat press ceramic. All specimens were subjected to shear bond strength test at a crosshead speed of 1.0 /min.
Results: The results of measured in Mean SD and data were analyzed by one-way AVOVA (p= .05) and Tukey HSD test (p= .05).: group FP 16.090 1.841 , group PC 12.620 1.8256 , group PCG 10.920 0.9283, significant differences between all groups (p< .05). Significant differences were found in each between group FP and group PC, group FP and group PCG (p< .05).
Conclusion: The shear bond strength of press-to-metal ceramic to porcelain fused non precious metal was described higher in unused gold bonder group than used gold bonder groups.