In the compacted bentonite containing Ag2O, the transport of iodide ion was investigated by Through-diffusion method. It is confirmed that Iodide ion is transported by diffusion process in the compacted bentonite containing Ag2O as well as in the compacted bentonite without Ag2O. However, the lag-time of iodide ion in the compacted bentonite containing Ag2O is larger than that in the compacted bentonite without Ag2O. The increase of the lag-time was observed in pure iodide ion solution and also in 0.1M NaCl-iodide ion solution. The apparent diffusion coefficient of iodide ion in the compacted bentonite containing Ag2O has lower value than that in the compacted bentonite without Ag2O. The effect of Ag2O on the effective diffusion coefficient was not clearly investigated in the compacted bentonite containing Ag2O while the values of effective diffusion coefficient of iodide ion in the compacted bentonite without Ag2O obtained in this study were similar to those in the compacted bentonite reported in the literature.

한국어

Ag2O를 첨가한 압축 벤토나이트에 대하여 관통 확산법으로 요오드 이온의 이동 특성을 관찰하였다. Ag2O를 첨가하지 않은 압축 벤토나이트와 마찬가지로 Ag2O를 첨가한 압축 벤토나이트에서도 요오드 이온은 확산에 의하여 이동하는데, Ag2O를 첨가한 압축 벤토나이트는 Ag2O를 첨가하지 않은 압축 벤토나이트에 비하여 요오드 이온의 초기 누출 시간이 지연되는 것으로 나타났다. Ag2O를 첨가한 압축 벤토나이트에서 요오드 이온의 초기 누출 시간 지연은 확산 용액으로 순수 요오드 이온 수용액을 사용하였을 때 뿐만 아니라 0.1 M NaCl-요오드 이온 수용액을 사용하였을 때에도 관찰되었다. 또한 Ag2O를 첨가한 압축 벤토나이트의 겉보기 확산 계수는 Ag2O를 첨가하지 않은 압축 벤토나이트의 겉보기 확산 계수보다 낮은 값을 나타내었다. Ag2O를 첨가하지 않은 압축 벤토나이트의 유효 확산 계수는 기존 문헌에 보고된 값 과 거의 일치하는 결과를 얻었으며, Ag2O를 첨가한 압축 벤토나이트에서 요오드 이온의 유효 확산 계수는 Ag2O 첨가에 따라 대체적으로 감소하는 경향을 나타내었다.