The experiment for nitrogen and phosphorus removal using olivine was carried out to investigate nitrogen and phosphorus removal effect and removal mechanism, and evaluated the application possibility of olivine as a material for environment-friendly hydraulic structure with nutrient salts removal. The removal efficiency of PO4-P, NH4-N, and NO3-N was 90.2%, 40.8% and 4.6% respectively, in the completely mixed batch reactor using powered olivine under the condition of initial concentration of 5 mg/L and the reaction time of 30 min. The removal rate of PO4-P was decreased to be 8.0% after it was 15.8~18.6% at the initial reaction time, but the NH4-N was hardly removed in the fixed continuous reaction using granular olivine for 30 days at the initial concentration of 5 mg/L and the space velocity of 1 h−1. Mg3(PO4)2·22H2O, MgHPO4·3H2O, Fe3(PO4)2(OH)2, Fe(PO4), struvite were observed in XRD analysis for the precipitate in completely mixed batch reactor.

한국어

본 연구는 천연광석인 감람석을 이용하여 수중의 질소와 인을 제거하는 실험을 수행하여 감람석의 질소와 인 제거효과를 확인하고 제거기작를 구명하여 영양염류 제거기능을 겸비한 친환경수공구조물의 재료로 감람석의 활용 가능성을 평가하기 위해 수행되었다. 분말 감람석을 이용한 회분식 완전혼합반응에서 초기농도 5 mg/L, 반응시간 30분 기준으로 PO4-P는 90.2%, NH4-N는 40.8%, NO3-N은 4.6%의 제거율을 나타내었다. 입상 감람석을 이용한 고정식 연속반응에서 초기농도 5 mg/L, 공탑속도 1 hr−1 기준으로 30일 운전한 결과 PO4-P는 반응초기에 15.8~18.6%의 제거율을 보이다가 8.0%로 점차 낮아졌으나 NH4-N는 반응기간 전체에 걸쳐 거의 제거되지 않았다. 완전혼합반응 침전물에 대한 XRD분석결과 Mg3(PO4)2·22H2O, MgHPO4·3H2O, Fe3(PO4)2(OH)2, Fe(PO4), Struvite의 생성이 관찰되었다.