This paper investigated the characteristics of wasteform containing a spent zeolite used as a separating agent of FPs for recycling LiCl waste which would be generated from pyrochemical process of spent PWR fuel. In this study, a conventional borosilicate and Ca-rich glass were used as a consolidating agent for spent zeolite and it's mixing ratio was changed in the range, 25 35wt%. The leach rates of Cs and Sr had about 0.1 0.01g/m2day and 0.001~ 0.0001g/m2day, respectively. The leach resistance of Cs increased with amount of SAP and it showed about 10 times higher in the Ca-rich glass wasteform than in the conventional borosilciate glass wasteform. The compressive strength of wasteform was affected with the amount of glass. Thermal expansion rate of containing 30wt% glass has relatively lower than others. Also, the melting temperature was little changed in given mixing ratio of glass.

한국어

본 연구에서는 전해환원공정에서 발생하는 폐용융염에서 LiCl을 재활용하기 위해 핵종제거 물질로 제올라이트를 사용할 때, 발생하는 폐제올라이트와 여기에 흡착된 유리염을 고감용으로 고화하는 경우의 고화체특성을 살폈다. 주종 핵종인 Cs의 침출속도는 붕규산유리보다는 석회유리로 고화한 경우, SAP과의 반응비와 유리의 첨가량을 변화시켜도 그 값은 1/10 정도로 낮았으며 그 범위는 0.1에서 0.01g/m2d이었다. 한편으로 Sr의 침출속도는 유리의 종류와 첨가량변화에 크게 지배를 받지 않으며 Cs보다 훨씬 낮은 0.001에서 0.0001g/m2d이었다. 그리고 압축강도는 유리의 함량이 증가할수록 감소하였고, 열팽창율은 어떤 온도에서 도 유리를 30% 함유한 것이 가장 적게 나타났다. 한편으로 이 고화체들의 용융온도는 약 1,100℃로서 유리의 함량이 증가하면 약간씩 높아졌다.