The purpose of this study is to analyze steel corrosion properties of ternary concrete according to mixing ratio of meta-kaolin. The specimens were made with various mixing ratio(5, 10, 15%) of meta-kaolin for fly ash, blast-furnace slag(5, 10, 15%) as ternary concrete, plain concrete and concrete containing fly ash, blast-furnace slag, meta-kaolin, silica fume(15, 20%) as binary concrete, which W/B ratio fixed 0.55. Compressive strength, coefficient of chloride diffusion, steel corrosion area ratio, steel weight reduction ratio were test. From the test results, ternary concrete containing meta-kaolin indicates a lower chloride migration coefficient than plain and binary concrete. And, the increaser containing ratio of meta-kaolin, the enhancer steel corrosion properties. Therefore, it has been confirmed that the ternary concrete containing meta-kaolin had a great synergy effect. Especially, ternary concrete of containing meta-kaolin 15% and blast-furnace slag 5% indicates the best steel corrosion properties.

한국어

본 연구의 목적은 메타카올린의 혼입률에 따른 3성분계 콘크리트의 철근부식 특성을 연구하는데 있다. 시험체는 메타카올린의 혼입률(5, 10, 15%) 각각에 대해 플라이 애쉬 및 고로슬래그(15, 10, 5%)를 혼입한 3성분계 콘크리트와 플레인 콘크리트 및 플라이애쉬, 고로슬래그, 메타카올린, 실리카흄을 혼입한 2성분계 콘크리트를 제작하였고, 물-결합재비는 55%로 고정하였다. 압축강도, 염화물 이동계수, 철근 부식면적률, 철근 질량감소율 등을 실험하였다. 실험결과에 따르면, 메타카올린을 혼입한 3성분계 콘크리트의 염화물 이동계수는 플레인 콘크리트 및 2성분계 콘크리트보다 낮게 나타났다. 그리고 메타카올린의 혼입률이 증가할수록 철근부식 특성이 향상되어, 3성분계 콘크리트의 시너지 효과를 확인할 수 있었다. 특히, 3성분계 콘크리트인 메타카올린 15%와 고로슬래그 5%를 혼입한 경우 가장 우수한 철근부식 특성을 나타내었다.