irconia-Frit composites의 소결 및 물성에 미치는 MgO 첨가의 효과

원문정보

Effect of MgO Addition Affecting in Zirconia-Frit Composites’ Sintering and Properties of Matter

권은자, 이규선

피인용수 : 0(자료제공 : 네이버학술정보)

초록

영어

This study sought to apply different MgO additions to Zirconia (20wt % Frit) and thereby determine its mechanical properties depending upon variation of temperature, as a part of elementary study. First, in terms of sintering density depending on sintering conditions, it was found that sintering density increased as temperature varied from 1100 to 1300 . As the addition of MgO increased, it was found that sintering density tended to decrease at each temperature. For the maximum sintering density obtained from pellet, it was found that 3wt% MgO addition specimens sintered at 1300 had its maximum sintering density as high as 97.39%. This study measured mechanical properties of these specimens, and it was found that their bending strength tended to decrease as the content of MgO addition increased. And it was found that their bending strength reached up to 162 MPa when 3wt% MgO was added to them for sintering process at 1300°ΔC. It was also found that those specimens had Vickers microhardness up to 4.6 GPa when 5wt% MgO was added to them for sintering process at 1300.

목차

[Abstract]
 I. 서론
 II. 연구재료 및 방법
  1. 연구재료
  2. 연구방법
 III. 연구 결과
  1. 소결 밀도
  2. 기계적 특성
 IV. 고찰
 V. 결론
 참고문헌

저자정보

  • 권은자 Eun-Ja Kwon. 혜전대학 치기공과
  • 이규선 Gyu-Sun Lee. 동남보건대학 치기공과

참고문헌

자료제공 : 네이버학술정보

    함께 이용한 논문

      ※ 기관로그인 시 무료 이용이 가능합니다.

      • 4,000원

      0개의 논문이 장바구니에 담겼습니다.