The characteristics of controlled drug release were studied for a biodegradable drug delivery system. A biodegradable chitosan matrix was prepared after swelling chitosan with 10%-acetic acid and adding sulfadiazine. The release behavior of sulfadiazine from the chitosan matrix was studied using the Higuchi's diffusion controlled model in phosphate buffer solutions of pH 7.4 and pH 1.2. The drug release time was delayed by increasing the content of sulfadiazine. The drug release at pH 7.4 was more delayed than that at pH 1.2. The reason is that chitosan has greater swelling abilities at low pH than at high pH. The apparent release rate constant(K) increased as the concentration of drug increased. In shoat, the formulation the biodegradable chitosan matrix to suppress the burst effect of drug release mechanism, which led to a sustained release pattern.

한국어

키토산을 10%-아세트산에 팽윤시킨 용액과 SD 를 인산염 완충용액에 녹인 용액을 흔합하여 키토산 매트릭스를 제조하였다. 키토산 매트릭스로부터 pH 7 7.4와 pH 1.2에서 약물방출 거통을 규명하고 지속적이고 조절된 약물방출형 제제로서의 사용 가능성 을 고찰하였다. 키토산 매트릭스내의 약물 함유량이 증가함에 따 라 약물 방출 시간이 늦어졌으며, pH 1.2에서보다 p pH 7.4에서 약물 방출 시간이 더 지연되었다. 그 이 유는 약물전달체가 엽기성 용액에서보다 산성 용액 에서 팽윤를 더 잘하기 때문이라고 생각된다. 약물 방출 속도에 있어서는 pH 7.4에서보다 pH 1.2에서 더 빨랐으며, 겉보기 방출속도상수(K)값도 역시 증가하였다. 결과적으로 본 실험에셔 약물전달체로 사 용된 키토산은 방출조절형 제제로서 그 가능성을 타진할 수 있었다.