The disposable glucose bio-sensor using composite of CTA and PCL membrane was developed for measurement of glucose. The most effective membrane was composed of CTA/PCL(80/20, w/w) and glutaraldehyde one-step immobilization method (10um thickness) for glucose sensor gave the best result among various methods, considering oxygen permeability and electronic sensitivity. A scanning electron micrograph of the cross-section of a typical asymmetric CTA/PCL composite membrane showed that the membrane fused with a dense layer covered with a GOD-glutaraldehyde. Glucose oxidase immoblilized on the membrane showed the linearity between difference of absolute amperometric values and glucose concentrations within 7mM when the GOD immobilized electrode was used. About 35% of activity was remained after 8 days when the tyrosinase was immobilized on CTA/PCL (80/20) membrane.

한국어

Glucose biosensor용 glucose oxidase 고정화 막의 단일화 벚 일회용의 간편화를 위한 연구로서, glucose oxidase의 고정화 대상막으로는 CTA와 PCL의 촌합비율이 80/20인 혼합막을 사용한 고저화 방법 중에서는 glutaraldehyde one-steD 방법으로 효소고정화층의 건조 전 두께가 10um 인 효소고정화 막이 효과적이었다. 이 고정화 막을 천자현미쇠 으로 관찰해 본 결과, 고밀도의 CTA/PCL 막층 위에 GOD-glutaraldehyde 층이 건조 후 3um 정도로 덮여 있는 것을 알 수 있었다. Dissolved oxygen전극을 사용하여 glucose농도의 증가에 따른 전류세기의 차이 값을 측정해 본 결과, glucose 7mM의 안도범위 내에서 선형성을 나타냈으므로 이 고정화원이 glucose sensor용 효소고정화 방법으로 가장 적합하였다. 한편, tyrosmase는 CTA와PCL의 혼 합비율이 80/20인 혼합막에 direct CDI 방법으로 고정화한 것이 가장 효과적이었으며, 8일 후에도고 정화된 tyrosmase의 활성이 35% 이상 유지되었다.