Characteristics of cell growth and poly(3-hydroxybutyrate-co-4-hydroxybutyrate) [P(3HB-co-4HB)] synthesis was investigated through flask and batch cultures of Alcaligenes latus and Comamonas acidovorans. The specific growth rate of C. acidovorans increased with yeast extract concentration and decreased with 1,4-butanediol concentration. Optimum glucose
concentration for growth of C. acidovorans was 20 g/L. In one-step flask cultures of C. acidovorans, final dry cell weight and PHA content decreased with the ratio of 1,4-butanediol to glucose, while the 4HB fraction in copolymers gradually increased to 100 mol% with an initial 1,4-butanediol concentration of 20 g/L as single carbon source. The specific growth rate of A. latus decreased with γ-butyrolactone concentration and optimum sucrose concentration for growth was 10 g/L. In batch cultures of A. latus, 4HB fraction increased with initial γ-butyrolactone concentration. P(3HB-co-4HB) with 19 mol% 4HB was obtained when the initial ratio of γ-butyloractone (g/L) to sucrose (g/L) was 10 : 10.

한국어

Alcaligenes latus와 Comamonas acidovorans의 플라스크 및 회분식 배양을 통하여 균체성장과 P(3HB-co-4HB) 합성 특성을 알아보았다. C. acidovorans의 비성장속도는 yeast extract 농도에 따라 증가하였고 1,4-butanediol 농도에 따라 감소하였으며, 최적 glucose 농도는 20 g/L였다. C.acidovorans의 1단 플라스크 배양에서 최종 균체농도 및 PHA 함량은 초기 1,4-butanediol : glucose의 비율이 증가함에 따라 감소하였으나 4HB 함량은 점점 증가하여 탄소원으로 1,4-butanediol 만을 20 g/L 공급하였을 경우 균체성장은 매우 낮았으나 100 mol%의 P(4HB) homopolymer를 얻을 수 있었다. A. latus의 비성장속도는 γ-butyrolactone 농도에 따라 감소하였으며, 최적 sucrose 농도는 10 g/L였다. A.latus의 회분식 배양에서 탄소원인 sucrose의 농도를 10 g/L로 고정하고 γ-butyloractone의 농도를 2~10 g/L까지 변화하여 실험한 결과 γ-butyloractone 농도가 증가할수록 4HB 함량 역시 증가함을 보였으며, 초기 γ-butyloractone (g/L) : sucrose (g/L)의 비가 10 : 10일 때 19 mol%의 4HB를 포함하는 P(3HB-co-4HB)를 얻었다.