Kraft Lignin which is produced abundantly in pulp industry, was chemically degraded into small oligomers and polymerized using horseradish peroxidase. Lignin acidolysis was optimized by controlling reaction time and HCl concentration. Acidolyzed lignin was polymerized and copolymers of acidolyzed lignin and phenol or p-cresol were synthesized. 70% of kraft lignin was
degraded after acidolysis. Number average molecular weight of all lignin polymers were from 8,500 to 14,000 and did not show large difference. Differential scanning calorimeter analysis showed that acidolyzed lignin polymer and copolymer of acidolyzed lignin and phenol or p-cresol had glass transition and melting temperature while lignin did not show any melting
temparature under 300℃, which indicates that newly synthesized lignin polymers can be used in industry under mild condition.

한국어

Kraft lignin을 산분해한 후 HRP를 이용하여 다시 중합시키거나, phenol과 p-cresol과 공중합을 시도하였다. lignin은 구조가 복잡하고 여러 가지 단량체로 이루어져 있어서 그 변형이 용이하지 않기 때문에, 구조를 보다 단순하게 하기 위하여 산분해라는 화학적인 방법을 통하여 lignin을 분해하였다. 반응시간과 HCl의 농도를 조절하여 최적의 분해수율을 유지하였다. 산분해를 통하여 얻은 고분자와 p-cresol 및 phenol을 HRP를 이용하여 공중합하여 수평균 분자량이 8,500～14,000인 공중합체가 얻어졌다.
DSC 검사 결과 새롭게 중합된 고분자들은 250℃ 근방에서 녹는점을 가지고 있었으며 열적 가공성이 용이함을 알 수 있었다.