Yttrium aluminum garnet (YAG), which possesses excellent properties, is investigated and applied. The sintering technology of YAG porous ceramics is optimized. Results show that the porosity initially increases and then decreases with an increase of increasing temperature rate, the porosity are decreased with an increase of removing carbon temperature, the porosity are decreased with an increase of sintering temperature, the porosity are decreased with an increase of holding time. Meanwhile, the compressive strength constantly exhibits an opposite tendency. The optimization of the sintering technology of YAG porous ceramics is based on porosity and compressive strength. A good sintering technology are an increasing temperature rate of 8 oC/min, a removing carbon temperature of 800 oC, removing carbon time of 1 h, a sintering temperature of 1450 oC and holding time of 2 h. The porosity of the prepared YAG porous ceramics is 57.4%, and the compressive strength is 8.89 MPa.